Features
- Excellent lubricity
- Excellent corrosion protection
- Air-curing
- High pressure and wear resistance
Composition
- Solid lubricants
- Organic binder
- Organic solvent
Applications
Excellent combination of lubrication and corrosion protection.
How to use
Surface preparation
Carefully clean and degrease surfaces to be coated with MOLYKOTE® 3402-C LF Anti-Friction Coating.
Recommended pretreatments: blasting or phosphating. Both pretreatments increase the adhesion and service life of MOLYKOTE® 3402-C LF Anti-Friction Coating
How to apply
Stir MOLYKOTE® 3402-C LF Anti-Friction Coating thoroughly before and during use, apply by spraying, dipping, centrifuging or brushing. Surfaces should be coated as evenly as possible. Recommended dry-film thickness: 5 to 20 µm.
Coverage
When applied at 10 µm dry-film thickness, MOLYKOTE® 3402-C LF Anti-Friction Coating has a coverage of approximately 12 m2/kg (this value does not take into account the losses generated during the application process).
Thinner
Recommended thinner is MOLYKOTE® L13 Thinner.
Typical properties
Specification writers: These values are not intended for use in preparing specifications. Please contact your local MOLYKOTE® sales representative prior to writing specifications on this product.
Standard(1) | Test | Unit | Result |
---|---|---|---|
Color | Gray | ||
Service temperature range | °C
°F |
-200 to 310
-328 to 590 |
|
Physical properties | |||
EN ISO DIN 2431 | Viscosity, cup #4 at 23°C (73°F) | s | 32 |
ASTM D1475 | Density at 23°C (73°F) | g/ml | 1.06 |
ASTM D56 | Flash point | °C
°F |
15
59 |
Load-carrying capacity, wear protection, service life(2) | |||
ASTM D2625 | Falex, procedure B, load-carrying capacity | N N N |
s=12,200 m=11,100 z=8,900 |
ASTM D2625 | Falex, procedure A, endurance life at 4,450 N load | min | s=193 m=225 |
ASTM D2714 | LFW-1, rotating, load=2,860 N @ 72 rpm, v=7.9 m/min, no. of revolutions to µ=0.1 | min | s=74,800 m=108,800 |
ASTM D2714 | LFW-1, oscillating, load=900 N @ 89.5 osc/min, no. of oscillations to µ=0.08 | s=63,400 m=227,600 z=33,800 |
|
Resistance(2) | |||
ASTM B117, DIN 50021 | Corrosion resistance without red rust (steel substrate, spraying application, film thickness = 10 µm)(3) | h | z=120 |
(1)ASTM: American Society for Testing and Materials. DIN: Deutsche Industrie Norm.
(2)Surface pretreatment: s=sandblasted; m=Mn-phosphated; z=Zn-phosphated.
(3)As the performance in corrosion protection is affected by the geometry of the parts, by the pretreatment of the surface, by the application method and by the thickness of the applied dry film, DuPont recommends customers run trials on original parts before setting specifications.
Curing
Typical curing conditions:
- Touch-dry after 5 minutes at 20°C (68°F)
- Fully cured after 120 minutes at 20°C (68°F)
Handling precautions
PRODUCT SAFETY INFORMATION REQUIRED FOR SAFE USE IS NOT INCLUDED IN THIS DOCUMENT. BEFORE HANDLING, READ SAFETY DATA SHEETS AND CONTAINER LABELS FOR SAFE USE, PHYSICAL AND HEALTH HAZARD INFORMATION.
Usable life and storage
When stored at temperatures between 0°C (32°F) and 23°C (73°F) in the original unopened containers, MOLYKOTE® 3402-C LF Anti-Friction Coating has a usable life of 36 months from the date of production.
Packaging
This product is available in different standard container sizes. Detailed container size information should be obtained from your nearest MOLYKOTE® sales office or MOLYKOTE® distributor.